Go Green polyurea waterproof coating is a homogeneous liquid made of high molecular polymer resin as the main agent, mixed with mineral fillers and additives. It has a wide range of applications, suitable for all waterproofing projects such as buildings, roofs, basements, toilets, swimming pools, reservoirs, etc. It can be constructed on any curved, inclined, flat and vertical surfaces, and has excellent physical and chemical properties, such as high tensile strength, high flexibility, wear resistance and aging resistance.
Features:
The material has high strength, large elongation, good elasticity, and strong ability to adapt to structural deformation;
The solidified body is dense and has high bonding strength;
It has high solid content and does not contain harmful solvents such as benzene, which is non-polluting to the environment and human body;
Liquid, cold construction, flexible and convenient construction methods;
Single-component construction is convenient, and the solidified body is resistant to water, corrosion, mildew, cold and impermeability.
Specification:
Go Green polyurea waterproof coating meet the basic performance requirement as below.
| Product Type | Polyurea | ||
| Main Ingredients | High molecular polymer resin, mineral filler, additives | ||
| Application Range | Leakage in structural cracks such as deformation joints, expansion joints, joints, settlement joints, etc. | ||
| Appearance | Homogeneous viscous liquid | ||
| Viscosity（25℃） | 3500-6500 mPas | ||
| Density | 1.45g/ cm³ | ||
| Application Time | 15 min | ||
| Surface Drying Time（23℃） | 30 min | ||
| Odor | No irritating smell | ||
| Construction Conditions | Avoid construction below 5℃； No visible water on the construction surface; The base needs to be cleaned in advance to remove slurry and dust | ||
| Product Performance Comparison | Tensile Strength | ＞1.2 MPa | |
| Elongation At Break | ＞150% | ||
| Tear Strength | ＞3 N/mm | ||
| Bonding Strength | ≥1.2 MPa | Dry Base | |
| ≥0.8 MPa | Wet Base Surface | ||
| Water Absorption | ≤1% | ||
| Low Temperature Bendability | -35℃ No Cracks | ||
| Waterproof | 0.3MPa，120 min，Impermeable | ||
| Elastic Recovery Rate | ≥90% | ||
| Strength Retention After Acid Treatment | ≥80% | ||
| Strength Retention After Alkali Treatment | ≥80% | ||
| Strength Retention After Salt Treatment | ≥80% | ||
| Elongation After Heat Treatment | ≥80% | ||
Application:
There should be no visible water on the project base surface, otherwise the water should be drained for 24 hours before construction;
It is advisable to construct at a temperature above 5℃, the construction site should be well ventilated, and fire-fighting equipment should be placed;
After opening the bucket, it should be used up as soon as possible, and the time should not exceed 15 minutes; it should not be directly exposed to the air for a long time to prevent crusting;
After opening the lid, the unused material should be immediately covered tightly, and the remaining material should be used up as soon as possible;
Before it is actually dry, pay attention to protecting the construction site.
Dosage is 1.5kg/m2, thickness is 1mm.
Storage:
The product should be stored in a clean, dry, and sealed bucket;
Transport according to the normal product requirements, prevent rain, exposure, squeezing, collision, and ensure that the packaging is intact;
The product should be stored in a ventilated, dry and cool place, avoid direct sunlight and rain. The storage temperature should not be higher than 40℃.
Under normal storage conditions, the shelf life is 6 months.
Package is 20kg/bucket